An in vitro Study to evaluate the Effects of Various Polymerizing Conditions on the Flexural Strength of Autopolymerizing Resins
Sanjeev Singh,, Abid Z Hussain,, RU Thombare,, BK Motwani,, Shweta Singh,
Citation Information :
Singh, S, Hussain, AZ, Thombare, R, Motwani, B, Singh, S. An in vitro Study to evaluate the Effects of Various Polymerizing Conditions on the Flexural Strength of Autopolymerizing Resins. J Health Sci Res 2017; 8 (1):15-19.
To investigate the effect of variation in temperature and time intervals on the flexural strength of two brands of autopolymerizing resins polymerized at constant pressure.
Materials and methods
Two autopolymerizing resins RR Cold Cure resin (DPI) and RR-Rapid Repair Powder (Dentsply) were used. A total of 20 samples were fabricated for each group. Samples were polymerized at temperature ranges of 40°, 50°, 60°, and 70°C and at time intervals of 5, 10, and 15 minutes in the customized curing pot, maintaining pressure of 30 psi.
Results
Flexural strength was verified using universal testing machine using three-point bending test and was then compared with all samples and also with the samples cured in open air (control group). The samples cured at higher temperature, i.e., 60° and 70°C, have shown increased strength than those at 40° and 50°C as well as control group. Time interval of 10 minutes is considered sufficient to increase the strength of the resin, as per the results of this study.
Conclusion
The samples cured under varied condition of time and temperature but under constant pressure showed increased strength than those cured in open air.
Clinical significance
The effect of pressure and temperature has been demonstrated, which could be utilized for enhancing the durability of the prosthesis fabricated from autopolymerized resins.
How to cite this article
Singh S, Hussain AZ, Thombare RU, Motwani BK, Singh S, Mangalekar SB. An in vitro Study to evaluate the Effects of Various Polymerizing Conditions on the Flexural Strength of Autopolymerizing Resins. J Health Sci Res 2017;8(1):15-19.
Effect of polymerization temperature and time on the residual monomer content of denture base polymer. Eur J Oral Sci 1998 Feb;106(1):588-593.
Residual monomer content and its release into water from denture base materials. Dent Mater 1995 Nov;11(6):338-342.
Influence of polymerizing conditions on the monomer elution and microhardness of autopolymerising polymethyl methacrylate resin. Eur J Oral Sci 2002 Apr;110(2):179-183.
The effect of preparation conditions of acrylic denture base materials on the level of residual monomer, mechanical properties and water absorption. J Dent 1995 Oct;23(5):313-318.
Conversions in denture base polymers. J Biomed Mater Res 1982 Sep;16(5):741-754.
The level of residual monomer in self-curing denture-base materials. J Dent Res 1983 Feb;62(2):118-120.
Linear distortion of acrylic resin. J Prosthet Dent 1985 Jan;53(1):53-55.
Complete denture relines with autopolymerizing acrylic resin processed in water under air pressure. J Prosthet Dent 1967 Aug;18(2):103-114.
Physical properties of acrylic resin polymerized by four different techniques. J Prosthet Dent 1985 Oct;54(4):522-524.
Fracture toughness of provisional resin for fixed prosthodontics. J Prosthet Dent 1987 Jul;58(1):23-29.
Effect of water temperature during polymerization on strength of autopolymerizing resin. J Prosthet Dent 2000 Aug;84(2):222-224.
(2005) Influence of polymerization method, curing process, and length of time of storage in water on the residual methyl methacrylate content in dental acrylic resins. J Biomed Mater Res B Appl Biomater 2006 Feb;76(2):340-345.